321 Λωρίδα από ανοξείδωτο χάλυβα
Προμήθεια Baogu κατηγορίας λαμαρίνας από ανοξείδωτο χάλυβα
| Τύπος | Βαθμός | Βαθμός | % χημικών συστατικών | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Αλλα | |||
| ωστενιτικό | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3,50-5,50 | 5.50-7.50 | ≤0,060 | ≤0,030 | - | ≤1,00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1,00 | - | ≤0,25 | - | ||
| 301 | 1.431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | ≤0,10 | - | |
| 304 | 1,4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304 λίτρα | 1,4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304Η | 1,4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1,4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316 λίτρα | 1,4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316Τι | 1,4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | 0.1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0.1 | - | |
| 317 λίτρα | 1,4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0.1 | - | |
| 321 | 1,4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 321Η | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1.455 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| 347Η | 1.494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| xm-19 | Nitronic50 | ≤0,06 | 20.50-23.50 | 11.50-13.50 | 4,0-6,0 | ≤0,045 | ≤0,030 | 1.50-3.00 | ≤1,00 | - | 0,2-0,4 | Σημ.: 0,10-0,30 V: 0,10-0,30 | |
| 904 λίτρα | N08904 | ≤0,02 | 19,0-23,0 | 23,0-28,0 | 4,0-5,0 | ≤0,045 | ≤0,035 | ≤1,00 | 0.1 | Cu: 1,0-2,0 | |||
| Διπλός | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤2,00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1,00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| * | S32760 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,00 | ≤0,030 | ≤0,010 | 3,0-4,0 | ≤1,00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21.5-24.5 | 3,0-5,5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1,00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1.446 | ≤0,08 | 23.00-28.00 | 2.00-5.00 | ≤1,00 | ≤0,040 | ≤0,030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Φερρίτης | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0,5 | ≤1,00 | ≤0,040 | ≤0,020 | - | ≤1,00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1,00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1,00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0,75 | ≤1,5 | ≤0,040 | ≤0,030 | 1,50-2,50 | ≤1,00 | - | ≤0,25 | - | |
| Μαρτενσίτης | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0,6 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1,25 | ≤0,060 | ≥0,15 | - | ≤1,00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1,50-2,50 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | 0,75 | ≤1,00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | 3.00-5.00 | - | Σημ. 0,15-0,45 |
| 631 | 17-7ΡΗ | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | ≤0,50 | - | Αλ 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3,50-5,50 | ≤1,00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1,00 | 2,5-4,5 | - | Αλ 0,75-1,50 | |
Περιγραφή
Η λωρίδα από ανοξείδωτο χάλυβα 321 είναι ένας τύπος ωστενιτικού ανοξείδωτου χάλυβα με χαμηλή περιεκτικότητα σε άνθρακα και καλή αντοχή στη διάβρωση σε πολλά διαβρωτικά περιβάλλοντα.Το 321 προσφέρει εξαιρετική ικανότητα συγκόλλησης, καλή μηχανική ικανότητα και εξαιρετικές ιδιότητες κατασκευής.
Η λωρίδα από ανοξείδωτο χάλυβα 321 χρησιμοποιείται συνήθως στη χημική βιομηχανία, στη βιομηχανία χαρτοπολτού και χαρτιού, στη ναυτιλιακή και υπεράκτια μηχανική, καθώς και στις βιομηχανίες τροφίμων και ποτών.
Η λωρίδα από ανοξείδωτο χάλυβα 321 έχει επίσης υψηλό επίπεδο αντοχής σε ρωγμές και σκασίματα λόγω διάβρωσης λόγω καταπόνησης χλωρίου.Είναι επίσης ανθεκτικό στο υδροχλωρικό οξύ σε υψηλές θερμοκρασίες έως 250°C (480°F).
Χαρακτηριστικά
Καλή αντοχή στη διάβρωση: Η λωρίδα από ανοξείδωτο χάλυβα 321 έχει καλύτερη αντοχή στη διάβρωση από τους τύπους ανοξείδωτου χάλυβα 304 και 316, γεγονός που την καθιστά ιδανική για χρήση σε διαβρωτικά περιβάλλοντα.
Εξαιρετική συγκόλληση: Η λωρίδα ανοξείδωτου χάλυβα 321 μπορεί να συγκολληθεί με όλες τις μεθόδους, συμπεριλαμβανομένης της συγκόλλησης με τόξο (TIG / GTAW), της συγκόλλησης με δέσμη ηλεκτρονίων (EBW / EFW), της συγκόλλησης με βυθισμένο τόξο (SAW) και της συγκόλλησης με δέσμη λέιζερ (LBIW).
Υψηλή αντοχή: Τα επίπεδα αντοχής της λωρίδας ανοξείδωτου χάλυβα 321 είναι έως και 50% υψηλότερα από αυτά των 304 τύπων ανοξείδωτου χάλυβα και έως και 80% υψηλότερα από αυτά των 316 τύπων ανοξείδωτου χάλυβα λόγω της αυξημένης περιεκτικότητας σε άνθρακα και του μεγέθους κόκκων ωστενίτη.