Πηνίο από ανοξείδωτο χάλυβα 316/316L/316Ti
Περιγραφή
| Τύπος | Βαθμός | Βαθμός | % χημικών συστατικών | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Αλλα | |||
| ωστενιτικό | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3,50-5,50 | 5.50-7.50 | ≤0,060 | ≤0,030 | - | ≤1,00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1,00 | - | ≤0,25 | - | ||
| 301 | 1.431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | ≤0,10 | - | |
| 304 | 1,4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304 λίτρα | 1,4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304Η | 1,4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1,4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316 λίτρα | 1,4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316Τι | 1,4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | 0.1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0.1 | - | |
| 317 λίτρα | 1,4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0.1 | - | |
| 321 | 1,4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 321Η | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1.455 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| 347Η | 1.494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| xm-19 | Nitronic50 | ≤0,06 | 20.50-23.50 | 11.50-13.50 | 4,0-6,0 | ≤0,045 | ≤0,030 | 1.50-3.00 | ≤1,00 | - | 0,2-0,4 | Σημ.: 0,10-0,30 V: 0,10-0,30 | |
| 904 λίτρα | N08904 | ≤0,02 | 19,0-23,0 | 23,0-28,0 | 4,0-5,0 | ≤0,045 | ≤0,035 | ≤1,00 | 0.1 | Cu: 1,0-2,0 | |||
| Διπλός | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤2,00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1,00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| * | S32760 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,00 | ≤0,030 | ≤0,010 | 3,0-4,0 | ≤1,00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21.5-24.5 | 3,0-5,5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1,00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1.446 | ≤0,08 | 23.00-28.00 | 2.00-5.00 | ≤1,00 | ≤0,040 | ≤0,030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Φερρίτης | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0,5 | ≤1,00 | ≤0,040 | ≤0,020 | - | ≤1,00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1,00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1,00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0,75 | ≤1,5 | ≤0,040 | ≤0,030 | 1,50-2,50 | ≤1,00 | - | ≤0,25 | - | |
| Μαρτενσίτης | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0,6 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1,25 | ≤0,060 | ≥0,15 | - | ≤1,00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1,50-2,50 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | 0,75 | ≤1,00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | 3.00-5.00 | - | Σημ. 0,15-0,45 |
| 631 | 17-7ΡΗ | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | ≤0,50 | - | Αλ 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3,50-5,50 | ≤1,00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1,00 | 2,5-4,5 | - | Αλ 0,75-1,50 | |
Προμήθεια Baogu κατηγορίας λαμαρίνας από ανοξείδωτο χάλυβα
| Φινίρισμα επιφάνειας | Χαρακτηριστικά και εφαρμογή |
| 2B | Η φωτεινότητα και η επιπεδότητα της επιφάνειας του no 2B είναι καλύτερη από το no2D.Στη συνέχεια, μέσω μιας ειδικής επιφανειακής επεξεργασίας για τη βελτίωση των μηχανικών ιδιοτήτων του, το No2B θα μπορούσε σχεδόν να ικανοποιήσει ολοκληρωμένες χρήσεις. |
| Νο. 1 | Γυαλισμένο με λειαντικό ιμάντα άμμου#100-#200, έχουν καλύτερη φωτεινότητα με ασυνεχείς χονδρές ραβδώσεις, χρησιμοποιούνται ως εσωτερικά και εξωτερικά στολίδια για κτίρια, ηλεκτρικές συσκευές και μαγειρικά σκεύη κ.λπ. |
| Νο.4 | Γυαλισμένο με λειαντικό ιμάντα άμμου #150-#180, έχουν καλύτερη φωτεινότητα με ασυνεχείς χονδροειδείς ραβδώσεις, αλλά πιο λεπτό από το Νο3, χρησιμοποιούνται ως κτίρια μπανιέρας εσωτερικά και εξωτερικά στολίδια ηλεκτρικές συσκευές μαγειρικά σκεύη και εξοπλισμός επεξεργασίας τροφίμων κ.λπ. |
| HL | Γυαλισμένο με λειαντικό ιμάντα άμμου #150-#320 στο φινίρισμα Νο.4 και έχει συνεχείς ραβδώσεις, που χρησιμοποιούνται κυρίως ως διακοσμητικά κτιρίων, ανελκυστήρες, πόρτα κτιρίου, μετωπική πλάκα κ.λπ. |
| BA | Ψυχρή έλαση, λαμπερή ανόπτηση και περασμένη με δέρμα, το προϊόν έχει εξαιρετική φωτεινότητα και καλή ανακλαστικότητα όπως καθρέφτης, συσκευές κουζίνας, στολίδι κ.λπ. |
| 8K | Το προϊόν έχει εξαιρετική φωτεινότητα και προτιμά η ανακλαστικότητα να είναι ο καθρέφτης. |